Nickel 201 Washers manufactured at TorqBolt are corrosion resistant,high temperature resistant with ultimate tensile strength.
Dimensional standards as per DIN 125,ISO 7089,ISO 7090,ISO 7092,DIN 433,DIN 7349,DIN 9021,ISO 7093, are provided.
The raw material of these fasteners is renowned as registered trademarks like Inconel,Incoloy,Incoloy Alloys. Being a PED certified Fasteners Manufacturer by TUV Rheinland,our fasteners are accompanied with EN 10204 3.1/3.2 certification. Nickel 201 Washers are available in hot forged,cold forged and bar stock machined conditions depending upon the order quantity.
Nickel 201 Is Commercially Unadulterated (99.6%) Fashioned Nickel Almost Similar To Nickel 200 With Lower Carbon Content To Resist Embrittlement By Intergranular Carbon At Temperatures Over 600 Degrees F (315 Degrees F) Its Lower Carbon Content Reduces Hardness, Making It More Suitable For Cold Farmed Items Or Applications.
Nickel 201 washers distribute clamp load over a wider bearing area, prevent surface damage, and accommodate bolt-hole oversize. TorqBolt manufactures Nickel 201 washers per ASME B18.21.1 / B18.22.1, DIN 125 / 126 / 127 / 9021, and ISO 7089 / 7090 / 7093 / 7094, in metric (M3–M100) and imperial (#4–4") sizes.
Plain Washer Dimensions
Nickel 201 plain washers are characterized by three critical dimensions: ID (clearance over bolt diameter), OD (load distribution area), and thickness (compressive stiffness). Standard tolerances are h13 on OD and H13 on ID per ISO 286-2; flatness 0.05 mm/100 mm and parallelism 0.05 mm/100 mm verified per lot. Edge break / chamfer per drawing.
Form Variants
Form A (regular) — DIN 125-A / ISO 7089, the default plain washer
Form B (large OD) — DIN 9021 / ISO 7093, for soft mating surfaces
Form C (heavy) — DIN 7349 / ISO 7094, for slotted holes / structural use
Spring (split) — DIN 127 / ASME B18.21.1, helical anti-vibration
Conical / Belleville (DIN 6796 / 2093) — preload maintenance
Hardness & Surface
Nickel 201 washers are hardness-controlled to balance load-distribution stiffness against surface damage to mating parts. Typical Vickers HV ranges: plain 140–180 HV; spring 380–440 HV; Belleville 460–540 HV. Surface finish Ra 1.6 µm or better; on critical sealing applications, Ra 0.8 µm available.
Special Patterns
TorqBolt produces Nickel 201 washers in square (DIN 436), fender (oversized OD), tab / lock-tang (DIN 462 / 463), and spherical seat washer + cup combinations. EN 10204 3.1 / 3.2 material certificates standard; NACE MR0175 / ISO 15156 on request.
Pure & Low-Alloyed Nickel
Commercially-pure nickel grades (UNS N02200, N02201) are used where the application demands maximum nickel chemistry purity: electrical conductivity, magnetostriction, hot-caustic resistance, or food / pharmaceutical contact. Pure nickel is non-magnetic above its Curie point, weldable without filler in thin sections, and resistant to dry chlorine, fluorine, and hot caustic solutions where stainless steels fail.
Nickel 200 (N02200, >99% Ni, max 0.15% C) is the general-purpose grade for chemical-process and electroplating equipment. Nickel 201 (N02201, max 0.02% C) is the low-carbon variant required for service above 315°C to prevent graphitization that would destroy mechanical properties. Nickel 205 is the magnetic-grade variant. Nickel 270 (N02270) is high-purity electronics grade.
Pure nickel fasteners are supplied per ASTM B160 (rod/bar) and AMS 4730 with EN 10204 3.1 / 3.2 certificates including chemistry, hardness (HV 100-160 annealed, up to 250 cold-worked), and tensile testing. NACE MR0175 sour-service is qualified in the annealed condition. Welding uses pure-nickel filler (ENi-1) with copper-oxide-free flux to prevent weld embrittlement.